Best galvanized steel wire rope is very common in our production and life, and different industries have different performance requirements for steel wire rope. The main function of steel wire rope is bundling and traction, and different environments have different requirements on the characteristics of steel wire ropes. For example, when used in coastal or sea water, the steel wire rope needs to be resistant to salt and alkali and has strong corrosion resistance, so Best galvanized steel wire rope is selected.

Best galvanized steel wire rope is coated with a zinc layer on the surface of a single steel wire to achieve corrosion resistance. Depending on the galvanizing method, there are electro-galvanized and hot-dip galvanized.

Hot-dip galvanizing and electro-galvanizing have this essential difference in process. Electro-galvanizing is obtained by applying an external power source and using electric accumulation to obtain the plating layer. The obtained coating is composed of fine pure zinc crystal grains. Generally, the amount of zinc on the electro-galvanized layer can reach 750gm2.
Hot-dip galvanizing relies on physical thermal diffusion to form a coating, first forming an iron-zinc compound, and then forming a pure zinc layer on the surface of the iron-zinc compound. The high value of zinc on hot-dip galvanizing is only 593g/m2. Hot-dip galvanizing is zinc plated in a molten zinc bath at 450-480 degrees.
Compared with cold galvanized zinc layer, hot-dip galvanized zinc layer has better corrosion resistance due to the zinc-iron alloy layer. The surface condition of Best galvanized steel wire rope is hot-dipped with zinc-iron alloy, so its color should be a little black. The electroplated surface has no chemical reaction, so it is still the original color of zinc, which looks brighter. In general, the zinc layer of hot-dip galvanizing is thicker, and the corrosion resistance is better. The zinc layer of electro-galvanized zinc is thinner and has poorer corrosion resistance. However, hot-dip galvanizing will reduce the mechanical properties of the steel wire, and galvanized steel wire ropes that require high strength and high corrosion resistance are mostly twisted by electro-galvanized steel wires.

Choose different Best galvanized steel wire rope according to different usage conditions. For example, the support steel wire in the water pipe is better electroplated, it looks good, and the cost is low; if it is a power tower, it should be hot-dip galvanized. Because hot-dip galvanizing has good corrosion resistance, it can be used for 30 to 40 years. Although the zinc content is high on the surface, the hot-dip galvanized steel wire rope has a layer of zinc-iron alloy on the surface, and its anti-corrosion ability is much higher than that of the cold galvanized steel wire rope.